4. Operation Guide
Removes by the painting rusty stain, the old varnish film etc, the basic plane request does not have rusts away, greasy dirt, oxide skin and so on unreliable attachment; The steel and iron surface may use spurts sand or pill to eliminate the rust, achieving the St3 level or the Sa2.5 level is the best; If the scene construction condition is limited, eliminates oil rust by steel wire brush and remover processing together; Use special-purpose cleansing agent to eliminate the old paint level, in order to guarantee the basic plane satisfied the construction request.
The painting environment dose not has sand dust, sleet, mist; maintenance basic plane clean is dry, painting under room temperature and clear weather. using brushes spreads, spurts spreads, rolls spreads or soaks spreads method and so on when spreads, according to the special details to select the corresponding method.
Elects evenly to brush spreads/Spurts spreads the primer, after waiting for the primer table done, again paints finishes. Each painting has the time-gap request, the list painting gap is 4 hours; If needed adjusting the coating viscosity, select the necessary special-purpose diluents.
5. Package, Storage and transportation
This packing in the iron bucket in seal in which models; the single package is 5kg, 10kg and 20kg.
This product should deposit in cleanly, dry, cool, ventilating place, avoids with the acid and alkali contact, prevent the rain drenches with the insulation exposes to the sun; the product storage time is a year.
When transported, should add grass rope, paper box or wooden crate packing outside the iron bucket, Avoid the force collision, prevent the leakage.
This product is flammable, strictly prohibits the smoke and fire.
Attach ：
Metal anticorrosion fluorine silicon coating technology performance chart
NO. Items Standard Test Method
1 Adhesion ability level ） 1 GB/T 1720—89
2 Flexibility （mm） 1 GB/T 1731—93
3 Hardness ≥0.4 GB/T 1730—93
4 Impact strength（kg.cm） ≥50 GB/T 1732—93
5 Acid resistance （10%H2SO4） Soaks 720h,Does not have bubbles, does not have falls off GB/T 1763—89
（10%HCI） Soaks 720h,Does not have bubbles, does not have falls off
6 Alkali resistance （30%NaOH） Soaks 720h,Does not have bubbles, does not have falls off GB/T 1763—89
7 Salt water resistance
（3%NaCL） Soaks 720h,Does not have bubbles, does not have falls off GB/T 1763—89
8 solvent oil resistance Soaks 720h,Does not have bubbles, does not have falls off GB/T 1734—93
9 Water proof Soaks 720h,Does not have bubbles, does not have falls off GB/T 1733—93
10 Wet hot (soggy ) resistance 500h，2 level GB/T 1740—89

svchem65@yahoo.com.cn

Comments

——The heat conduction performance is fine, prompt releasing arrangement quantity of heat, prevents the heat energy accumulation and the hyperpyrexia, not flammable has from extinguishes the nature, is flame-resistant the effect to be remarkable, reaches the FV-0 level;
——High strength, high adhesion, elimination coating and equipment air gap, Prevents the acid, the alkali, the salt and the atmosphere to the material corrosion;
——Moisture-proof, hydrophobic water repellency, Bears the ozone, bears the ultraviolet ray, Bears the radiation, Bears the aging, May realize exempts the maintenance long period movement;
——its takes shape, the easy to operate, suits in the heterogeneous type equipment and the component surface protection and special electric contact spot insulation protection processing.
 Qualification
This in view of the electricity, the electric power and the related profession to the equipment and the primary device insulation protection, the heat conduction, is flame-resistant with the heat resistance is moisture-proof and so on the request, drew up the enterprise standard "Organ silicon To be flame-resistant heat conduction High Voltage Insulation Coating Technical standard" (Q/SV 11-2001), The routine inspection and the pattern examine qualified (for details sees technical specification data sheet) completely.
 Range of Application
It is suitable for losing in the electrical power Transmission system in the High Voltage the mother arrange, putting on the wall drive pipe, the high efficiency electrical machinery, the dry type transformer, the switch cabinet, outside the electric cable prime need insulates, the heat conduction, is flame-resistant, the moisture-proof protection equipment and the primary device, particularly in the electrical part which in contamination, in the moist environment.
This has the fine construction characteristic, Carries on to the geometry shape complex primary device surface spreads seals the protection effect to be remarkable, Its physics and chemistry target performance is better than hotly contracts the drive pipe.
 Operation guide
To be spread the spot surface to carry on the convention to sweep clear, decontamination and degreasing, fat processing, keep its surface clean. This is the single component coating, even spread with the hair brush either the same tool spreads in is spread the equipment or the primary device must protect the spot. Spreads brushes one coating thickness is 0.5 millimeter generally, may according to the actual need, grasps spreads brushes the number of times and rubber thickness. The coating should leak proof spread, not dribble, does not hang the silk.
When the coating uncaps the use, if has not used up, should turn off the lid immediately, the seal preservation next time again will use.
 Package , storage , and transportation
The product packing or models is packed in the airtight metal flexible hose, As storing maintains dry and ventilates, prevented all day exposes to the sun, the rain drenches. The storage period is 6 months, after surpasses the storage time, after duplicate examined qualified still may use.
Please accord to non- dangerous material storage and transportation.
FR60 series organ silicon is flame-resistant the heat conduction high pressure insulation coating Technical index Chart
NO. Items Standard Index Accordance with test
1 outward appearance Red, light green, yellow, and white sticks the thick mobile liquid GB 1721-79
2 viscosity CP 5000~10000 GB 265-88
3 Vulcanizing time 25℃ RH50%） a. surface dry up time ≤30min
b. full dry up time ≤48h GB 6753.2-86
4 tensile strength ,MPa, ≥1.5 GB 528-76
5 Pulls apart the elongation ratio ,% ≥150 GB 528-76
6 Adhesion Ability
(cycling method, Level ) 1~2 GB 1720-89
7 Hardness （S） ≥20 GB 531-76
8 Anti Flaming value Conforms to the FV-0 level IEC 60707:1981
9 Coefficient of thermal conductivity w/m•K ≥0.15 GB 11205-89
10 Volume Electric resistance Ω•m ≥1.0×1014 GB 1410-78
11 Surface Electric resistance Ω•m ≥1.0×1012 GB 1410-78
12 breakdown field strength MV/m ≥18 GB 1408-78
13 The heat resistant (-40~200℃/2.5h•5 delimits circle law determination from now on) Is not bigger than 2 levels DL/T627-97
14 Artificial accelerate ageing 1000h appraise No less middle degree GB 1865-80
15 Chemical reagent resistance
(acid, alkali, salty reagent function) Does not have the skin, falls off, bubbles, changes color and so on the phenomenon GB 1763-89
16 operational temperature range -50℃~200℃ In fact application appraise

svchem65@yahoo.com.cn

Comments

B. Structure and use
climbs skirt is silicon fluorine rubber product. It is the only producer in china. It is detected by national authority institution. Its insulatibity, hydrophobic and mobility etc. are all better than general rubber products. When use in normal temperature, bond the umbrella skirt and porcelain by silicon fluorine bond. Attention to fill by bond at the opening joint, don’t leave clearance, make the umbrella skirt and porcelain to one thing. Clear odd bond after planish. The power can run after the surface is dry.

C. Size
Number Specification (mm) Number Specification (mm)
1 Ø 50×Ø 270 30 Ø 275×Ø 510
2 Ø 95×Ø 240 31 Ø 280×Ø 486
3 Ø 96×Ø 240 32 Ø 280×Ø 490
4 Ø 110×Ø 340 33 Ø 280×Ø 520
5 Ø 125×Ø 310 34 Ø287×Ø 575
6 Ø 140×Ø 375 35 Ø 300×Ø 460
7 Ø 140×Ø 380 36 Ø 305×Ø 560
8 Ø 150×Ø 365 37 Ø 305×Ø 470
9 Ø 150×Ø 367 38 Ø 314×Ø 487
10 Ø 150×Ø 370 39 Ø 320×Ø 500
11 Ø 150×Ø 375 40 Ø 325×Ø 545
12 Ø150×Ø 380 41 Ø 345×Ø 540
13 Ø 150×Ø 385 42 Ø 345×Ø 565
14 Ø 150×Ø390 43 Ø 355×Ø560
15 Ø 150×Ø 490 44 Ø 360×Ø 510
16 Ø 160×Ø490 45 Ø 380×Ø 555
17 Ø 163×Ø 455 46 Ø 425×Ø 650
18 Ø 165×Ø455 47 Ø 427×Ø 675
19 Ø 167×Ø 380 48 Ø 430×Ø 590
20 Ø 170×Ø380 49 Ø 465×Ø 700
21 Ø 170×Ø 410 50 Ø 490×Ø 735
22 Ø173×Ø 467 51 Ø 510×Ø 745
23 Ø 173×Ø530 52 Ø 520×Ø 800
24 Ø 175×Ø 465 53 Ø 530×Ø 715
25 Ø 210×Ø425 54 Ø 545×Ø 766
26 Ø215×Ø 455 55
27 Ø270×Ø 475 56
28 Ø 275×Ø 485 57
29 Ø 275×Ø465 58
D. Bond
a) Clear
Use clean cloth wipes the surface of porcelain, wipe off defilement.
b) Preassemble
Please choose the umbrella skirt which inner diameter match up with the porcelain and the outer diameter accord with the request, carry on packing.
c) Rubberize
Well-distributed rubberize on the surface of the scraper (about 0.5mm). Apply the bond of the same thickness at the opposite of umbrella skirt.
d) Suit
Case the rubberized umbrella skirt and well placed. Even press the surface in order to remove the air in the joint surface, remove odd bond.
E. Package and deposit
a) Pack with the box.
b) Decide the package number according to the different size of umbrella piece. Attach the introduction and inspection certificate.
c) Pack the bond by itself.
d) Deposit it at dry place, avoid contacting with oil and other harmful material.
e) Don’t pile up over three floors. Avoid breaking the package through transport.
f) Pay attention to avoid breaking the umbrella skirt by sharp weapon when open the box.
F. Order notice
a) Notice the type, size, number and deliver date in the order.
b) Contact unit: Hebei Silicon Valley Chemical Co., Ltd, High Voltage Electric Factory
Direct-current suspended type porcelain
Insulator increases climbs skirt
A. Purpose
Direct-current suspended type porcelain insulator increases climbs skirt is a new product of our company, special used in increase climb of direct current or alternating current suspended type insulator. The capacity usage and bond procedure are similar as above-mentioned increase climb umbrella skirt, but different with the structure.

B. Size
Model FSX1—160 FSXZ1—210 FSXZ1—300 FSXZ2—160
Suit specification KN Direct – current 160 Direct – current 210 Direct – current 300 Direct – current 160
Manufacture Tangshan NGK Tangshan NGK Tangshan NGK Dalian Porcelain Co.,Ltd
Increases Climb Skirt Climb distance mm 303 303 349 303
Increasing climb distance mm 185 185 193 180
Splice Area mm 884 884 1418 955
Increases Climb Skirt Weight Kg 2.2 2.2 3.1 2.2
Use glue consult quantity g 80 80 120 80
C. Increases climb skirt model explanation
FS——Product material structural style code, expressed the high temperature curing fluorine silicon material increases crawls the skirt.
X——Product characteristic code: the expression is suitable the direct-current suspended type porcelain insulator to increase climb skirt.
1——The expression is suitable the Tangshan NGK manufacture the porcelain insulator
2——The expression was suitable the porcelain insulation which made in Dalian.
3——Porcelain insulator intensity rank is 160、210、300 .
Other factory production porcelain, the glass spacer block may refer to the above target to select and purchase increase climbs skirt.
D. Bond
a) Chose the suit increase climb skirt in the table according to the insulator’s size.
b) Work should be in the environment of sunshine, no rain and snow, the temperature is not bellowing five degree centigrade.
c) The bond way is similar as above-mentioned.
E. Package and deposit
a) Pack with the box.
b) In the box, it has five pieces increase skirts, five pieces lap pieces, bond, inspection certificate and introduction.

svchem65@yahoo.com.cn

Comments

svchem65@yahoo.com.cn

Comments

1. The characteristic and the performance
• The fine hydrophobic character and fast, is balanced the hydrophobic migratory nature which, continues;
• The anti-flashover the voltage to be high, The anti- electric arc, bears leaks the mark, the electrical insulating property is fine;
• The high module, high strength, excels in the adhesion, High corrosion tolerance, Satisfied condition overhaul request;
• Bears the ozone, bears the ultraviolet ray, bears the environment aging, Does not get up the skin, Does not crack, The effective running time is long;
• Single component normal temperature solidification, In -20 ℃ still might construct, Easy to operate, In the normal maintenance time exempts sweeps clear, The efficiency is high.
2. Main qualification
This equates use department sign DL/T627 "electrical power system Anti flashover Coating with Normal temperature Solidification Silica gel", And has drawn up higher enterprise standard QB/SV09 "The RTV Insulator Anti flashover Coating" and QB/SV08 "RTV Coating Construct control Standard" comes the standard product the production and the construction application.
3. Range of application
This is suitable for rated voltage 0~750kV,Ambient temperature -50 ℃ ~200 ℃,Under the contamination condition moves junction, direct current system, Mainly uses in the power supply bureau transformer substation, the power plant booster station and loses the distribution line insulator and the chemical industry, the steel and iron, the electric railway, the mine pit and all easy contamination, the easy mist, to pour water on the moist electrical equipment, Enhances the equipment outside to insulate the rank, prevents the flashover accident the occurrence.
4. Operation Guide
Before the construction carries on the convention to the porcelain insulator or the glass surface to sweep clear, Decontamination and degreasing, fat processing, The maintenance surface clean is clean. May use to spurt spreads or brushes spreads the way to carry on the construction, Coating thickness should regard the scene contamination degree but to decide, Thickness 0.3 ~ 0.5mm, The coating should leak proof spread, not dribble, does not hang the silk. When the coating uncaps the use, If has not used up, Should cover securely immediately, The airtight preservation next time again will use.
5. Packages and Storage
This product packing in airtight metal container, when storing and transportation should maintain dry and ventilates, Prevented all day exposes to the sun, the rain drenches. The storage time is 1 year, Duplicate surpassed the storage time after to examine qualified still may use.

RTV The insulator antifouling Flashover the coating technical specification data sheet
Item DL/T 627 Standard Technical Property
（Test Value ） Test Method
Outward appearance Does not have the obvious mechanical impurity, does not have the cotton wool shape precipitation, after the solidification smooth smoothly does not have the air bubble White (red, ash, is transparent) the color mobile liquid, the coating smoothly does not have the air bubble GB 1721-79
Solid content % ≮22 55 GB 1725-89
Viscosity s 15~60 30 GB 1723-93
Surface resistivity
Ω•m ≮1×1012 1.8×1016 GB 1410-78
Volume resistivity Ω•m ≮1×1014 1.5×1014
Relative permittivity dielectric lose tangent value ≯3.0 2.35 GB 1409-78
≯0.3% 3.0×10-3
Breakdown field value MV/m ≮15 25.6 GB 1408-78
Arc resistance s ≮180 190 GB 1411-78
Resistance to track
and erosion TMA ≥2.5 1A 2.5 GB 6553-86
Adhesion ability （drawing the cycle method ） No less 2 level 1~2 level GB 1720-89
Abrasion resistance g ≯0.05 qualified; GB 1768-89
Rate of water absorption % ≯0.25 0.16 GB 1738-89
Hydrophobicity Hydrophobic angle >90° 111.6° DL/T627-1997
Corrosion proof Under the acid, the alkali, the salt and the transformer oil function do not have the corrugation, falls off, bubbles, changes color and so on The experiment does not have the corrugation to fall off bubbles changes color the phenomenon GB 1739-89
GB 1763-89
The labor frequency arc-over voltage (dryly flashover , wet flashover ) KV Has the coating insulator not to have the coating insulator not to have relatively to reduce Have coat 90.3 ,
no coat 89.5 GB 775-87
Have coat 52.0 ,
no coat 49.6
Flashover resistance U1（have paint coat）/U2
（no paint coat ）>1.5 2.34（average） GB 4585.1-84
The environment aging performance resistance The coating should not be cracked under the natural condition, the pulverization, the skin and falls off After the sample moves for 10 years the coating to be complete, has the good hydrophobic character GB11206-89
Artificial accelerate ageing Coating after 1000h artificial accelerated ageing test, is intermediate at least 1000h the salt-fog test does not have has flowed the severance according to GB/T1766 evaluates is 1 level GB1865-80
Heat resistant denaturation experiment (adhesive force) Bears 5 times of temperature cycles , the experiment but does not damage Translation failed! please try again. DL/T627-1997
Vulcanizing time Surface dry up ≯30 min Surface dry up 25 min GB 6753.2-86
Full dry up ≯7days Full dry up 72h

svchem65@yahoo.com.cn

Comments

]]> Tue, 22 May 2007 14:14:39 +0800 http://svchem650.nireblog.com/post/2007/05/22/prtv-anti-flashover-compound-coating http://svchem650.nireblog.com/post/2007/05/22/prtv-anti-flashover-compound-coating PRTV outside power equipment insulates with takes shape permanence anti flashover compound coating
PRTV outside power equipment insulates with takes shape permanence anti flashover compound coating, is a kind of electrical power system uses the new electrical function material, it’s specially for the electrical network and each round, loses, uses electricity the customer to be lasting eliminates the equipment flashover thoroughly the hidden danger then to design, It’s developed jointly by the North China electric power academy of science with our company successfully. The product has the unique chemical composition and the structure, achieved and surpasses the heat vulcanization silicon rubber physics electrical specification, Overall performance and so on more outstanding water repellency nature, as well as 20 years design service life has provided a kind of new technical measure for the electric porcelaneous equipment permanence counter- dirt.

1. Product Execution Qualification
This uses the North China electric power group company standard "Outside the Power equipment To insulate with Takes shape the Permanence Anti flashover the Compound Coating (PRTV) To use Leads Then", With Hebei silicon valley chemical industry limited company standard Q/HGH 019-2004 “Outside PRTV Power equipment Insulates with Takes shape Permanence Anti flashover Compound Coating" to organize the product the production and the construction.
2. Range of application
This product mainly uses in the electrical power system transformer substation and the transmission line insulator, the power plant and the electric power user changes outside the electricity equipment as well as other electrical equipments insulates lastingly anti flashover . After the porcelain (or glass) the insulator uses this product, Forms the porcelain (or glass) the skeleton complex effect, Enhances one kind of standardized disposition plan which outside the power transformer equipment insulates. Is suitable in alternating and direct circuit system rated voltage 1~750kV, Environment Temperature -50℃~ +50℃, Under the contamination condition moves outside the transformer substation and the impractical transmission line equipment insulates antifouling, Prevention flashover, Enhances the equipment outside to insulate the rank.
3. Operation Guide
To porcelain (or glass) insulator superficial thorough clear dirt, Removes the contamination, the fat and other attachments, After waits the electric porcelaneous surface pure to be dry, May use to spurt spreads or brushes spreads and so on to spread spreads the method to carry on the construction, Coating thickness is 0.5 ~ 0.6mm, the coating should leak proof spread, not dribble, does not hang the silk, The surface is smooth, levels also does not have the air bubble. Originally has used the RTV equipment, Should be clean the unreliable attachment cleaning up, remove the contamination, After uses the special-purpose processing medicinal preparation to clean, Again executes spreads PRTV.
4. Package and Storage
This product packing in airtight metal container, When storing and transportation should maintain dry and ventilates, Prevented all day exposes to the sun, the rain drenches. The storage time is 1 year, Duplicate surpassed the storage time after to examine qualified still may use when the coating uncaps the use, if has not used up, Should cover securely immediately the airtight preservation.

PRTV outside power equipment insulates with takes shape permanence anti flashover compound coating Technology parameter data sheet
Items Q/HGH 019-2004 Standard Technical Property （Test） Test method
Outward appearance
Does not have the obvious mechanical impurity and the cotton wool shape, The coating should level, be smooth also does not have the air bubble Toughness liquid, Does not have the impurity and the cotton wool shape, The coating is smooth also does not have the air bubble GB 1721-1979
Viscosity s 100~200 160 GB 1723-1993
Dielectric Strength kV/mm ≮25 32.3 GB 1408-1978
Surface resistivity Ω•m
Volume resistivity Ω•m ≮1×1012 4.25×1013 GB 1410-1978
≮1×1014 2.92×1015
Relative permittivity dielectric lose tangent value ≯3.0 2.7 GB 1409-1978
≯0.3% 2.5×10-3
Arc resistance s ≮180 217 GB 1411-1978
Electricity wear and tear leaks AC
Alternating current ≮TMA 4.5 1A 4.5 GB 6553-1986
DC
Direct current ≮TMA 3.5 1A3.5
Adhesion ability Cementation shearing strength MPa ≮3.0 4.7 GB 13936-1992
Cycling method level No less 2 level 1 GB1720-1989
Abrasion resistance g ≯0.05 0.035 GB 1768-1989
Ratio of Water absorption % ≯0.25 0.15 GB 1738-1989
Hydrophobicity Hydrophobic
and level Qav≥100°Qmin≥90°HC1~2 106°~109° HC1 DL/T810-2002
Lose property 96h Qav≥90°Qmin≥85°HC3~4 Non showing loss
recovery characteristic t≤24h
Water repellency characteristic 96h Qav≥110°Q min≥100°HC2~3 14 h Hydrophobicity reach HC1 110°~115°
Erosion Resistance Test Acid , alkali and salt , 80℃24 h Does not have the corrugation, falls off, bubbles, changes color and so on, The adhesion is not lower than 2 levels Does not have the corrugation, falls off, bubbles, changes color the phenomenon, The adhesion is 1 level GB 1763-1989
transformer oil 105℃24 h Does not have the corrugation, falls off, bubbles and so on, The adhesion is not lower than 2 levels Does not have the corrugation, falls off, bubbles the phenomenon, The adhesion is 1 level GB 1739-1989
Labor frequency arc-over voltage Dry arc-over voltage kV Has the coating insulator not to have the coating insulator not to have relatively to reduce Paint-coat 79.2 , no 75.9 GB 775-1987
Wet arc-over voltage kV Paint-coat 61.9, no 55.9
Flashover resistance test U1(have paint-coat )/U2(no paint-coat )≥2.0 U1 /U2 =2.23 GB 4585.1-1984
Heat resistant denaturation experiment -40℃~+80℃，2.5h×5 times The coating should not damage, The adhesion inspection is not lower than 2 levels After the experiment the coating does not have bubbles, the dehiscence, falls off, Adhesion 1 level DL/T627-1997
Salt Spray test 1700 h The test specimen does not surpass 3 time has flowed the severance After 1800h，Does not have has flowed the severance GBT5892-2003
GB/SV023-2003
Does not have leaks the mark, The electricity wear and tears have not reached the porcelain glaze Does not have leaks the mark, The wear and tears have not reached the glazed surface
Hydrophobic migration characteristic HC2~3 level HC1~2 level
A row line of experiment passes ≥3.0MPa 3.5 MPa
Flame Resistance FV-O level FV-O level GB/T13488-92
The longitudinal strength and pulls apart the elongation ratio Strength MPa ≮4.0 5.5 GB/T528-1988
elongation % No less 350 390
peel strength kN/m ≮12.0 17.5 GB/T529-1988
Hardness (Shao ) 35~55 46 GB/T531-1999
Vulcanizing time Surface Dry up min 20~50 35 GB6753.2-1986
Full dry up h ≯72 65
storage stability 50℃ ≥45days After 60 days ，A row line of experiment passes GB6753.3-1986
Self Clearance property [Only requests antifouling] After the dirty fluid cementation is dry, Strips the intensity ≯3kPa(1 level ) Peel off strength 2.3kPa(1 level ) QB/SV021-2003
Anti –icing property [Only requests to guard against the ice] Anti- regelation (measure) Paint-coat ice cover measure /no paint-coat ≯30% 18.3% QB/SV022-2003
hydration property DC value ≮90% 91.2%

svchem65@yahoo.com.cn

Comments

]]> Tue, 22 May 2007 14:13:46 +0800 http://svchem650.nireblog.com/post/2007/05/22/high-absorbing-water-solid-leak-stopping-agent-for-drilling http://svchem650.nireblog.com/post/2007/05/22/high-absorbing-water-solid-leak-stopping-agent-for-drilling High Absorbing Water Solid Leak Stopping Agent for Drilling
High absorbing water solid leak stopping agent have the strong function of absorbing water and stopping leak, which apply to the work of the leak of wall in drilling .it is a new environmental protection product with non-toxic, harmless, the non-pollution.
1. Production Description
This product has the ability of absorbing water quickly, and inflating continually, that apply to many kinds of couples rock layers and crack and the limestone caves. Be effective quickly, seal successfully, maintain long and anti-warm strongly the same time with the function of falling the water losing.

2. performance index
Item Index
SB-Ⅰ(thick parcel ) SB-Ⅱ(thin parcel) SB-Ⅲ(powder)
appearance Light yellow parcel Light yellow parcel White to light yellow powder
PH value 7~8 7~8 7~8
Wet value ≤10 ≤10 ≤10
Parcel diameter ＜10 ＜6 ＜1
Absorbing water rate ≥80 ≥80 ≥50

3. package deposit transport
Every three bag packed together with paper-plastic bag with the adhesive tape sealing the mouth. It’s each net weight 25±0.5Kg.
Please deposited in the storehouse. Please keep the storehouse airing and dry.
Please prevent the product from sun and squeezing and breakage.
Guarantee period is 2 years.

svchem65@yahoo.com.cn

Comments

]]> Tue, 22 May 2007 14:12:23 +0800 http://svchem650.nireblog.com/post/2007/05/22/sf150p-fluorine-silicon-drilling-liquid-thinner-powder http://svchem650.nireblog.com/post/2007/05/22/sf150p-fluorine-silicon-drilling-liquid-thinner-powder SF150P Fluorine Silicon Drilling Liquid Thinner (powder)
In order to satisfy the need of drilling, we research and develop high-temperature drilling liquid thinner, which is convenient to carriage and usage. It is a kind of black mobile solid powder which has the excellent nature of lowing stick and function of fastening wall against collapse. It also has function of disperser, lubrication, and antifoaming to the drilling fluid system, and control hydrating shale and improve mudding function of drilling fluid. It’s maintaining time last long after dealing the mud. This kind of product is green and environmental Protection with non-toxic, and non-pollution.

1. Performance index
Item Index
Appearance Black mobile solid powder
PH value 8~11
Wet value ≤15
Stick falling rate % 90 ± 2 ºC quantity addition 1% (percent by quality) ≥80
120 ± 2 ºC quantity ageing addition, 2.0% ( percent by quality) ≥75
2. Application scope and method
This product mainly apply to All kinds of drilling liquid exporting oil and gas, and geophysical survey, in order to fall the stick of the system ,and improve the quality of mud pie and fall the water loss in the filtering process ,which have the function of stabling the well wall.
It’s applying to freshwater drilling fluid, saltwater drilling fluid, high calcium drilling fluid and high solid drilling fluid.
According to the need of using drilling fluid progress, add our product and pump even then operate.
3. Package deposit transport
Packed with plastic bag whose net weight is 25KG/bag then every three bag put into paper-plastic bag.
Notice to be against breakage, bite by rats, leakage and wet in the process of storage.
It is non-flammability，non-explosion，non-toxic and harmless. Transport management according to non-dangerous product

svchem65@yahoo.com.cn

Comments

]]> Tue, 22 May 2007 14:11:34 +0800 http://svchem650.nireblog.com/post/2007/05/22/sf150-fluorine-silicon-drilling-liquid-thinner http://svchem650.nireblog.com/post/2007/05/22/sf150-fluorine-silicon-drilling-liquid-thinner SF150 Fluorine Silicon Drilling Liquid Thinner
SF150 Fluorine silicon Drilling Liquid Thinner is produced by our company and applies to drilling between 0~3000 meter. it has excellent performance of falling stick and fastening wall against collapse and function of lubrication and eliminate buff. It’s maintaining time last long after dealing the mud. This kind of product is green and environmental Protection with non-toxic, and non-pollution.

1. Performance index
item Index
appearance Black mobile solid powder
PH value ≤ 12
Stick falling rate % 90 ± 2 ºC quantity addition (percent by volume) ≥75
120 ± 2 ºC quantity addition 2.0%( percent by volume) ≥70

2. Package
It’s packing with 200L iron barrel, each barrel 200±1% KG.
3. Transport
Please accord to indangerous product.
4. Deposit
Notice to be against leakage and frostbit in the process of storage.

svchem65@yahoo.com.cn

Comments

]]> Tue, 22 May 2007 14:10:39 +0800 http://svchem650.nireblog.com/post/2007/05/22/sf-fluorine-silicon-filtrate-reducer-for-drilling-fluids http://svchem650.nireblog.com/post/2007/05/22/sf-fluorine-silicon-filtrate-reducer-for-drilling-fluids SF Fluorine Silicon Filtrate Reducer for Drilling Fluids
This product is the oil field chemical and mud aids which has the function of minimizing the waster loss and preventing well collapse. This production mainly composes by natural mineralizer and many kinds of fine industrial chemicals, which this kind of product is green and environmental Protection with non-toxic, and non-pollution. It is the widespread used aids.
A. Production Description
1. Silicon stability agent has strong ability of anti- temperature. The drilling mud still has very good function of failing water and anti-pollution when the temperature is higher than 180℃.
2. Excellent mud viscosity reduction rate, rheological adjustment and the high speed of progress.
3. Fastening wall against collapse well, reducing the abnormal situation occurrence as far as possible.
4. Saving other material, synthetically economic efficiency is better when used with SF260 Fluorine Silicon High-temperature Drilling Liquid Thinner together.
B. Performance index
Table1 physic-chemical performance
item Index
appearance Black mobile solid powder
PH value ≤ 12
Triage amount % ≤ 5
Drying lose amount % ≤ 15

Table 2 drilling performance
item Index
Mud filter loss ml 25 ± 2
apparent viscosity mPa.s 6 ～ 8
Drilling fluid filter loss of Sample additive 1% ml ≤ 14
Apparent viscosity of Sample additive 1% mPa.s ≤ 8
Shall inflection falling rate % ≥25
C. Package transport deposit
Every three bags in a paper-plastic bag which is sealed by gummed tape, each bag net weight 25 Kg±1%. Notice to be against leakage.
It is non-flammability, non-explosion, non-toxic and harmless. Transport management according to non-dangerous product.

svchem65@yahoo.com.cn

Comments

]]> Tue, 22 May 2007 14:08:15 +0800 http://svchem650.nireblog.com/post/2007/05/22/sf200p-fluorine-silicon-high-temperature-drilling-liquid-thinner-powder http://svchem650.nireblog.com/post/2007/05/22/sf200p-fluorine-silicon-high-temperature-drilling-liquid-thinner-powder SF200P Fluorine silicon High-temperature Drilling Liquid Thinner (powder)
In order to satisfy the need of drilling, we research and develop high-temperature drilling liquid thinner, which is convenient to carriage and usage. It is a kind of black mobile solid powder which has the excellent nature of lowing stick and function of fastening wall against collapse. It also has function of disperser, lubrication, and antifoaming to the drilling fluid system, and control hydrating shale and improves mudding function of drilling fluid. It’s maintaining time last long after dealing the mud. This kind of product is green and environmental protection with non-toxic, and non-pollution.

1. Performance index
item Index
appearance Black mobile solid powder
PH value 8~11
Wet value ≤15
Stick falling 90 ± 2 ºC quantity addition 1% (percent by quality)
≥80
2. Application scope and method
This product mainly apply to All kinds of drilling liquid exporting oil and gas、and geophysical survey, in order to fall the stick of the system ,and improve the quality of mud pie and fall the water loss in the filtering process ,which have the function of stabling the well wall.
It’s applying to freshwater drilling fluid, saltwater drilling fluid, high calcium drilling fluid and high solid drilling fluid.
According to the need of using drilling fluid progress, add our product and pump even then operate.
3. Package deposit transport
Packed with plastic bag whose net weight is 25KG/bag then every three bag put into paper-plastic bag.
Notice to be against breakage, bite by rats, leakage and wet in the process of storage.
It is non-flammability, non-explosion, non-toxic and harmless. Transport management according to non-dangerous product.

svchem65@yahoo.com.cn

Comments

]]> Tue, 22 May 2007 14:07:22 +0800 http://svchem650.nireblog.com/post/2007/05/22/sf260-high-temperature-drilling-liquid-thinner http://svchem650.nireblog.com/post/2007/05/22/sf260-high-temperature-drilling-liquid-thinner SF260 High-temperature Drilling Liquid Thinner
1. Production Description
SF260 Fluorine Silicon High-temperature Drilling Liquid Thinner is the new technologic production which we researched by our research and develop institution. This production is firstly created home by us and has been checked by experts, and its technology has the lead at home and has achieved international advanced level. It is National intellectual property institution award patent of invention. The core ingredient is copolymer which transform from special chemical reaction of organic silicon and organic fluorine, which make the product excellent nature of resisting hyperthermia and lowing stick.
This production has ultra strong ability to dilute and fall stick in the mud that surpass ability of the hard chromic salt, and its prominent characteristic is anti-hyperthermia, anti-salt, anti-calcium, besides above ,it has the function of disperser, lubrication, and antifoaming to the drilling fluid system, and control hydrating shale and improve mudding function of drilling fluid. When the mud density is 1.5 g/cu.cm, the product still have good stability, and the mud maintenance processing time last more than 7days. Also reducing gelatin intensity and shearing force and enhance greatly efficiency of well drilling. This kind of product is green and environmental Protection with non-toxic, and non-pollution. Have obtain the experts’ consistent high praise and have been the first choice in well drilling project after applying to all kinds deep wells of geological structure.

2. Performance index
Item Index
Appearance Black and adhesive fluid
PH value ≤ 12
Stick falling rate % 90 ± 2 ºC increase quantity 1% (percent by quality) ≥ 75
180 ± 2 ºC increase quantity 1.5%( percent by quality) ≥ 70

3. Package
This production is packed in iron barrel, each barrel net weight is 200KG ±1%. Also we can arrange package according to customer’s requirement.
4. Transport
It is non-flammability, non-explosion, non-toxic and harmless. Transport management according to non-dangerous product.
5. Deposit
Notice to be against leakage and frostbit in the process of storage.
svchem65@yahoo.com.cn

Comments

]]> Tue, 22 May 2007 14:06:13 +0800 http://svchem650.nireblog.com/post/2007/05/22/silicon-stability-agent-for-drilling-fluids http://svchem650.nireblog.com/post/2007/05/22/silicon-stability-agent-for-drilling-fluids Silicon Stability Agent for Drilling Fluids
This product is the oil field chemical with non-toxic; harmless, transforming from chemical industrial many times material polymerization reaction in stage. Making the mud has the function of hydrophobic capillary, preventing shale inflation effectively, improving friction of the mud pie, falling the interaction of clay particles, and equipping the dilution effect that reflect the having been merit .it is widespread to use in drilling.

A. Production Description
1. Silicon stability agent has strong ability of anti- temperature. The drilling mud still have very good fluidity when the temperature is higher than 150℃.
2. Excellent mud viscosity reduction rate, rheological adjustment and the high speed of progress.
3. Fastening wall against collapse well, reducing the abnormal situation occurrence as far as possible.
4．The amount used few, the effect well, the maintaining time long, saving other material, synthetically economic efficiency is better.
B. performance index
Item Index
Appearance Brown to depth brown liquid
PH value ≤ 12
Effect contain （CH3SiO3/2） % ≥10.0
Free alkali contain % ≤8.0
The room temperature falls sticks rate
(sample addition 2%） % 70
90℃ falls sticks rate (sample addition 3%）% 60
C. package
It’s packing with 200L iron barrel, each barrel 250Kg±2.5Kg. If has special requests, negotiated separately.
D. deposit
Notice to be against leakage.
E. transport
It is non-flammability、non-explosion、non-toxic and harmless. Transport management according to non-dangerous product.

svchem65@yahoo.com.cn

Comments

]]> Tue, 22 May 2007 14:05:17 +0800 http://svchem650.nireblog.com/post/2007/05/22/sfb-1-biology-thickening-agent-for-drilling-agent http://svchem650.nireblog.com/post/2007/05/22/sfb-1-biology-thickening-agent-for-drilling-agent SFB-1 Biology Thickening Agent for Drilling Agent
Drilling agent composed of many kinds of chemicals industrial materials without toxic, harm which is green product. It is used widely in drilling.

A. Production Description
1. SFB-1 biology thickening agent for drilling agent has strong ability of anti- temperature. The drilling mud still has very good stability when the temperature is higher than 150℃. It has the feature of contain low, thickening high, and suspension high.
2. SFB-1 biology thickening agent for drilling agent has the good feature of falling water losing, dissolving even, and improving the thick, anti-shearing, and anti-polluted.
3. SFB-1 biology thickening agent for drilling agent be preparation job site. Maintaining and processing is simple. For example, preparing the non-solid drilling agent doesn’t harm the reservoir.
4. After using SFB-1 biology thickening agent for drilling agent, the drilling agent materials is singularity, the cost is low, and the economic efficiency is better.
B. Performance index
Item Index
Appearance White to light yellow flow powder
PH value 7 ~ 9
Drying lose amount % ≤10

mud apparent viscosity mpa.s 8~10
filter loss ml 26~30

Drilling agent
(room temperature) apparent viscosity (sample additive amount
0.2%) mpa.s ≥35
Filter loss (sample additive amount 0.2%)
ml ≤10

Drilling agent
(180℃ boiling till 16h) apparent viscosity (sample additive amount
0.2%) mpa.s ≥30
Filter loss (sample additive amount 0.2%)
ml ≤15
C. Package deposit transport
It’s packed with transparent plastic bag inner, with plastic woven bag outside. Each bag net weight is 25±1%Kg.
It is non-flammability, non-explosion, non-toxic and harmless. Transport management according to non-dangerous product.
Notice to be against leakage and wet.

svchem65@yahoo.com.cn

Comments

]]> Tue, 22 May 2007 14:03:58 +0800 http://svchem650.nireblog.com/post/2007/05/22/dsa-1-surface-active-agent-for-drilling-fluid http://svchem650.nireblog.com/post/2007/05/22/dsa-1-surface-active-agent-for-drilling-fluid DSA-1 Surface Active Agent for Drilling Fluid
Using the surface active agent in drilling fluid is a important trend in mud technology. Because of some active agent have the function of changing the wet of the clay surface. After using professional surface active agent in the mud can improve stability of the system in high temperature, reduce the amount of the dealing agent, falling the high temperature loss water, improve the quality of mud pie, reduces bit balling and sticks calorie probability, that reduces the mud an elasticity, has prominently falls the PV effect to the high density mud.

1. Introduction
DSA—1 make Fluorine substitute for hydrogen and form carbon fluorinelipophilic group active agent which equip good stability and chemical inertness and “three high” “two hydrophobic”, that display that reduces the mud surface tension large scale, enhances the stability in heat temperature and mud lubricating ability, fall the stick cut strength and losing water in heat temperature, reducing the maintaining cost.
2. Mainly performance index
Mainly performance index
item Index
appearance White to milk white paste
PH value 6~8
density 1.0±0.2
Press filtering and losing water amount in freshwater mud ml ≤15.0
surface tension falling rate in distilled water % ≥50
3. Package deposit transport
Packing with barrel coating zinc, each barrel net weight is 100±1Kg
It’s deposited in the storehouse .keeping the storehouse airing and dry.
It’s preventing the product from sun and squeezing and breakage.
It is non-flammability, non-explosion, non-toxic and harmless. Transport management according to non-dangerous product.

svchem65@yahoo.com.cn

Comments

]]> Tue, 22 May 2007 14:01:58 +0800